Has anyone tried to sinter nylonx?

  • Trying to make a water tight print & even though print layers/lines look good it still somewhat porous. Was wondering if a sinter in the oven would get all the layers to bond together better.

  • MatterHackers


    As far as I am aware, we have not yet tried to sinter the prints after they have been completed but I would suspect that if you were to sinter the model then you would get tighter models. The key is to find the right temperature and time needed to get good bonding without melting the model down.

    If anyone has happened to have tried this I would like to see the results!